detail view sample V06_023
| drying method (details): | Lufttrocknung mit anschließender Ofentrocknung bei 105°C |
|
|||||
| wet weight | 576.2 g | weight under water | 25.2 g | ||||
| Atroweight after oven drying | 77 g | dry weight calculated | 75.6 g | ||||
| Umax | 648.0 % | degree of degradation | 1 | ||||
| residual density | 0.14 g/cm3 | volume (water displacement) | 551.00 cm3 | ||||
| nail spacing | before | after | shrinkage |
| radial | 40.0 mm | 40.0 mm | -0.10 % |
| tangential | 54.3 mm | 50.0 mm | 7.90 % |
| longitudinal | 80.2 mm | 68.0 mm | 15.20 % |
| volume shrinkage: | 21.90 % | ||
| volume (previous state) | 546.89 cm3 | volume (final state) | 187.73 cm3 | volume shrinkage | 65.70 % |
| surface (previous state) | 473.23 cm2 | surface (final state) | 384.32 cm2 | Surface change | 18.80 % |
| radial cut surface (previous state) | 5450.75 mm2 | radial cut surface (final state) | 732.89 mm2 | radial shrinkage | 86.60 % |
| tangential cut surface (previous state) | 6996.97 mm2 | tangential cut surface (final state) | 3947.22 mm2 | tangential shrinkage | 43.60 % |
| longitudinal measurement (previous state) | 151.86 mm | average length change | -2.87 mm | longitudinal shrinkage | 3.78 % |
|
|||||
| pre-drying | 4 Monatige Lufttrocknung bei Raumklima (ca. 22°C, 30-40%rF) bis zur Gewichtskonstanz | |
| Dry weight | 84 g | |
| post-drying | 24-stündige Ofentrocknung bei 105°C, Wägung nach direkter Entnahme aus dem Ofen | |
| Atro weight | 77 g | |
» back