detail view sample V19_001
| drying method (details): | Lufttrocknung mit anschließender Ofentrocknung bei 105°C |
|
|||||
| wet weight | 8170 g | weight under water | 942.5 g | ||||
| Atroweight after oven drying | 2705 g | dry weight calculated | 2827.5 g | ||||
| Umax | 202.0 % | degree of degradation | 2 | ||||
| residual density | 0.36 g/cm3 | volume (water displacement) | 7227.50 cm3 | ||||
| nail spacing | before | after | shrinkage |
| radial | 68.2 mm | 61.6 mm | 9.70 % |
| tangential | 94.3 mm | 77.8 mm | 17.50 % |
| longitudinal | 148.3 mm | 144.1 mm | 2.90 % |
| volume shrinkage: | 27.60 % | ||
| volume (previous state) | 7425.24 cm3 | volume (final state) | 4545.79 cm3 | volume shrinkage | 38.80 % |
| surface (previous state) | 3044.34 cm2 | surface (final state) | 2756.91 cm2 | Surface change | 9.40 % |
| radial cut surface (previous state) | 19838.19 mm2 | radial cut surface (final state) | 13426.90 mm2 | radial shrinkage | 32.30 % |
| tangential cut surface (previous state) | 25177.83 mm2 | tangential cut surface (final state) | 17418.48 mm2 | tangential shrinkage | 30.80 % |
| longitudinal measurement (previous state) | 262.54 mm | average length change | -1.92 mm | longitudinal shrinkage | 1.46 % |
|
|||||
| pre-drying | 4 Monatige Lufttrocknung bei Raumklima (ca. 22°C, 30-40%rF) bis zur Gewichtskonstanz | |
| Dry weight | 2911 g | |
| post-drying | 24-stündige Ofentrocknung bei 105°C, Wägung nach direkter Entnahme aus dem Ofen | |
| Atro weight | 2705 g | |
» back