detail view sample V19_015
| drying method (details): | Lufttrocknung mit anschließender Ofentrocknung bei 105°C |
|
|||||
| wet weight | 9980 g | weight under water | 1577.5 g | ||||
| Atroweight after oven drying | 4350 g | dry weight calculated | 4732.5 g | ||||
| Umax | 129.0 % | degree of degradation | 3 | ||||
| residual density | 0.51 g/cm3 | volume (water displacement) | 8402.50 cm3 | ||||
| nail spacing | before | after | shrinkage |
| radial | 98.8 mm | 90.3 mm | 8.60 % |
| tangential | 120.3 mm | 98.3 mm | 18.30 % |
| longitudinal | no value | no value | no value |
| volume shrinkage: | no value | ||
| volume (previous state) | 8536.91 cm3 | volume (final state) | 5954.11 cm3 | volume shrinkage | 30.30 % |
| surface (previous state) | 2589.16 cm2 | surface (final state) | 2538.19 cm2 | Surface change | 2.00 % |
| radial cut surface (previous state) | 27125.82 mm2 | radial cut surface (final state) | 23402.83 mm2 | radial shrinkage | 13.70 % |
| tangential cut surface (previous state) | 19335.73 mm2 | tangential cut surface (final state) | 14088.86 mm2 | tangential shrinkage | 27.10 % |
| longitudinal measurement (previous state) | 165.88 mm | average length change | 0.06 mm | longitudinal shrinkage | -0.07 % |
|
|||||
| pre-drying | 4 Monatige Lufttrocknung bei Raumklima (ca. 22°C, 30-40%rF) bis zur Gewichtskonstanz | |
| Dry weight | 4650 g | |
| post-drying | 24-stündige Ofentrocknung bei 105°C, Wägung nach direkter Entnahme aus dem Ofen | |
| Atro weight | 4350 g | |
» back