detail view sample V25_016
| drying method (details): | Lufttrocknung mit anschließender Ofentrocknung bei 105°C |
|
|||||
| wet weight | 873.8 g | weight under water | 49.3 g | ||||
| Atroweight after oven drying | 166 g | dry weight calculated | 147.9 g | ||||
| Umax | 426.0 % | degree of degradation | 1 | ||||
| residual density | 0.20 g/cm3 | volume (water displacement) | 824.50 cm3 | ||||
| nail spacing | before | after | shrinkage |
| radial | 52.3 mm | 47.3 mm | 9.50 % |
| tangential | 68.9 mm | 47.9 mm | 30.50 % |
| longitudinal | 89.2 mm | 88.3 mm | 0.90 % |
| volume shrinkage: | 37.70 % | ||
| volume (previous state) | 827.90 cm3 | volume (final state) | 520.21 cm3 | volume shrinkage | 37.20 % |
| surface (previous state) | 587.07 cm2 | surface (final state) | 468.02 cm2 | Surface change | 20.30 % |
| radial cut surface (previous state) | 5055.03 mm2 | radial cut surface (final state) | 3119.64 mm2 | radial shrinkage | 38.30 % |
| tangential cut surface (previous state) | 6996.53 mm2 | tangential cut surface (final state) | 3572.31 mm2 | tangential shrinkage | 48.90 % |
| longitudinal measurement (previous state) | 137.97 mm | average length change | -1.66 mm | longitudinal shrinkage | 2.41 % |
|
|||||
| pre-drying | 4 Monatige Lufttrocknung bei Raumklima (ca. 22°C, 30-40%rF) bis zur Gewichtskonstanz | |
| Dry weight | 179 g | |
| post-drying | 24-stündige Ofentrocknung bei 105°C, Wägung nach direkter Entnahme aus dem Ofen | |
| Atro weight | 166 g | |