detail view sample V28_027
| drying method (details): | Lufttrocknung mit anschließender Ofentrocknung bei 105°C |
|
|||||
| wet weight | 1382.44 g | weight under water | 46.4 g | ||||
| Atroweight after oven drying | 165 g | dry weight calculated | 139.2 g | ||||
| Umax | 738.0 % | degree of degradation | 1 | ||||
| residual density | 0.12 g/cm3 | volume (water displacement) | 1336.04 cm3 | ||||
| nail spacing | before | after | shrinkage |
| radial | 39.9 mm | 26.4 mm | 33.80 % |
| tangential | 47.5 mm | 15.7 mm | 67.10 % |
| longitudinal | 77.9 mm | 71.0 mm | 8.90 % |
| volume shrinkage: | 80.10 % | ||
| volume (previous state) | 1333.06 cm3 | volume (final state) | 235.17 cm3 | volume shrinkage | 82.40 % |
| surface (previous state) | 698.97 cm2 | surface (final state) | 301.59 cm2 | Surface change | 56.90 % |
| radial cut surface (previous state) | 7870.58 mm2 | radial cut surface (final state) | 2831.65 mm2 | radial shrinkage | 64.00 % |
| tangential cut surface (previous state) | 5733.77 mm2 | tangential cut surface (final state) | 247.61 mm2 | tangential shrinkage | 95.70 % |
| longitudinal measurement (previous state) | 89.97 mm | average length change | -5.82 mm | longitudinal shrinkage | 12.94 % |
|
|||||
| pre-drying | 4 Monatige Lufttrocknung bei Raumklima (ca. 22°C, 30-40%rF) bis zur Gewichtskonstanz | |
| Dry weight | 175 g | |
| post-drying | 24-stündige Ofentrocknung bei 105°C, Wägung nach direkter Entnahme aus dem Ofen | |
| Atro weight | 165 g | |
» back