detail view sample V30_Exp01
drying method (details): | Lufttrocknung mit anschließender Ofentrocknung bei 105°C |
wet weight | 93.2 g | weight under water | 4.78 g | ||||
Atroweight after oven drying | 16.5 g | dry weight calculated | 14.34 g | ||||
Umax | 465.0 % | degree of degradation | 1 | ||||
residual density | 0.19 g/cm3 | volume (water displacement) | 88.42 cm3 |
nail spacing | before | after | shrinkage |
radial | 18.2 mm | 14.3 mm | 21.60 % |
tangential | 23.7 mm | 16.6 mm | 29.80 % |
longitudinal | 30.8 mm | 27.3 mm | 11.40 % |
volume shrinkage: | 51.20 % |
volume (previous state) | 88.00 cm3 | volume (final state) | 49.54 cm3 | volume shrinkage | 43.70 % |
surface (previous state) | 109.93 cm2 | surface (final state) | 79.86 cm2 | Surface change | 27.40 % |
radial cut surface (previous state) | 1470.39 mm2 | radial cut surface (final state) | 1068.92 mm2 | radial shrinkage | 27.30 % |
tangential cut surface (previous state) | 1121.60 mm2 | tangential cut surface (final state) | 604.55 mm2 | tangential shrinkage | 46.10 % |
longitudinal measurement (previous state) | 43.28 mm | average length change | -1.98 mm | longitudinal shrinkage | 9.15 % |
pre-drying | 4 Monatige Lufttrocknung bei Raumklima (ca. 22°C, 30-40%rF) bis zur Gewichtskonstanz | |
Dry weight | 17.7 g | |
post-drying | 24-stündige Ofentrocknung bei 105°C, Wägung nach direkter Entnahme aus dem Ofen | |
Atro weight | 16.5 g |
» back